Micromechanical Modeling of AlSi10Mg Processed by Laser-Based Additive Manufacturing: From as-Built to Heat-Treated Microstructures
(2022-08-13)
The unique microstructure of the alloy AlSi10Mg produced by the laser-based powder bed fusion of metals (PBF-LB/M) provides high-strength and high-strain-hardening capabilities of the material. The microstructure and mechanical properties of 3D-printed, i.e., additively manufactured, AlSi10Mg are significantly altered by post-building heat-treatment processes applied in order to tailor the final properties of the parts. Using an accurate computational model to predict and improve the mechanical performance of 3D-printed ...
Aufsatz
Investigation of processing windows in additive manufacturing of AlSi10Mg for faster production utilizing data-driven modeling
(2022-04-29)
To reduce production time and decrease production cost, the increase of layer thickness is an adequate option in powder bed fusion. In order to determine the relationships between process parameters in laser powder bed fusion (PBF-LB/M) and final porosity in AlSi10Mg, samples were processed following a space-filling experimental design in the present study. A total of 144 samples were fabricated considering layer thicknesses of 30 µm, 45 µm, 60 µm, and 90 µm. Afterwards, porosity was assessed using image analysis and ...
Aufsatz
A comparative study using water atomized and gas atomized powder in laser powder bed fusion process – Assessment of the fatigue performance
(2022)
Gas-atomized (GA, spherical) and water-atomized (WA, spattered) commercially pure iron (cp-Fe) powders were processed using laser-based powder bed fusion, resulting in a slightly higher porosity of the WA condition. In addition to characterization of quasi-static mechanical properties, fatigue tests, which are known to be detrimentally affected by porosity, were finally considered, revealing good properties even for the WA condition. In terms of microstructure stability, the GA and WA specimens significantly differ; ...
Aufsatz
Oxide Modified Iron in Electron Beam Powder Bed Fusion - From Processability to Corrosion Properties
(2022-03-07)
Additive manufacturing (AM) processes are not solely used where maximum design freedom meets low lot sizes. Direct microstructure design and topology optimization can be realized concomitantly during processing by adjusting the geometry, the material composition, and the solidification behavior of the material considered. However, when complex specific requirements have to be met, a targeted part design is highly challenging. In the field of biodegradable implant surgery, a cytocompatible material of an application-adapted ...